MPPZn/AlH Metallized Film

Coating a thin Al/Zn layer on the surface of plastic film, will get high self-healing Al/Zn metallized film for capacitor use.
The prominent feature of metallized film is its self healing ability. That is, when somewhere is breakdown, short-circuit current can make the film around the breakdown area melting and evaporation to recover its insulation property. Thus significantly reduce the impact on the breakdown strength by conductive defects and weakness in paper or film, thereby improving the working field.
Generally the thickness of the metal layer is 5nm-50nm, but on the international it can be 1nm-100nm. In terms of heat resistance, 1nm-100um is preferred, while ideration of electric properties, 5nm-50nm is more preferred.

Quantity:

1、Features:
     Under the same evaporation conditions, the larger the coating thicknessδ, the smaller square resistance (Ω/□) , the smaller the resistance R, the greater the load current, while the worse self healing properties.

Al/Zn metallized film use heavy edge evaporation method, greatly reduce the contact resistance between the spraying area and the cores of the film capacitors, which has improved the quality of the capacitors.

Al/Zn metallized film has a better pressure resistance.

Al/Zn metallized film has a worse moisture resistance, easily oxidized.

2、Types of Metallized Layer
  Zn Al
Margin size(mm):1.0±0.5、1.5±0.5、2.0±0.5、2.5±0.5、3.0±0.5、4.0±0.5、5.0±0.5
Coating square resistanceΩ/□):Heavy-edge area3±1;Non heavy-edge area:(67.5)±30%
 

3、Cores

  1. Material:Plastic
  2. Width:Film Slit Width±0.3mm
  3. Inner Diameter:75mm +1.0mm/-0.5mm

4、 Roll Outer Diameter

roll outer diameter


   5、Specifications of MPPZn/AlH metallized film
性能
Properties
單位
Unit
要求
Requirements
密度Density g/cm3 0.905±0.005
厚度 Thickness µm 3.8 ~ 15
抗拉強度
Tensile Strength
縱向MD
(MPa)
≥100
斷裂伸長率
Elongation at Break
縱向MD
(%)
40 ~ 200
熱收縮率
Heat Shrinkage
縱向MD
(%)
≤5 ( 120°C, 10min)
( 120°C , 10 min )
介電強度
Break-dowm voltage
V/µm ≥350 ( 23°C, DC )
介電損耗因數
Dissipation Factor
- ≤4×10-4 (20℃,1KHz )
RC ΩF ≥5×104


     6、Packing

  1. Roll films are packed in vacuum plastic bag
  2. Bags are marked with lables of types
  3. The bags are packed in carton cases
  4. The cartons are wrapped in wooden cases or reinforced carton  

7、 Storge:

1、Metallized film should be stored in its original package until its use with temperature 5 ~35℃and humidity less than 85%RH.

2、Metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened.

3、The recommended temperature is 15 -25℃with humidity less than 60%RH after the package is open.

4、With original sealed package, and stored in the above mentioned conditions, the storage time can be as following:

Al metalized Film: 12 months from the delivered date

Al/Zn Alloy metalized Film: As Zn is relatively unstable, preservation period depends on the resistance of the film:

Less than 10 Ohms: 6 months (from delivery date)

10 Ohms to 15 Ohms: 3 months (from delivery date)

15 Ohms: 1months (from delivery date)

 


?Add: No.695 North Taishan Road,Tongling,Anhui,China     Tel: 86-562-2822518      Fax: 86- 562-2826278      Post Code:244000     E-mail:[email protected]
?Copyright © 2015,Tongling Tongfei Technology Co.,Ltd. All Resolved SITE MAP
新剑侠情缘贴吧 十三水规则 山东时时彩开奖视频直播 青海快三走势图图 24点游戏规则 彩票中心的手机投注客户端 尚合国际 淘宝快3技巧 点亮英雄杀图标 体彩福建36选718099期 北京赛pk10官网下载 怎么样通过淘宝刷单赚钱 足彩半全场开奖 贵州快3一定牛下载 宁夏11选5开奖结果今天 3d彩票投注规则 重庆时时开彩龙虎和开奖